Product description, mainly related to the product introduction and some table parameters, can be combined with graphics and text, and the content can be added, modified and deleted in the background column content management. Products can customize fields, and support dynamic fields and product subsidiary table information. Greatly enhance the practicality and applicability of the system, you are welcome to use it!
Color:
Net Weight：
Personal Purchase:
- * Description:
-
PLA Silk Resin is a high-performance silk masterbatch suitable for 3D printing. It is blended with pure PLA at a certain ratio and can be processed and formed through standard 3D printing extrusion equipment. The extruded filament has a stable diameter, high gloss, and good toughness. It supports high-speed printing and is specially designed for FDM 3D printing extrusion applications.
- * Product introduction video
-
- * Print model
-
TECHNICALDATA SHEET
PLA resin is a new type of fully biodegradable material made from renewable plant resources such as corn. The starch raw material is saccharified into glucose, which is then fermented with specific strains to produce high-purity lactic acid. This lactic acid is polymerized into PLA with a certain molecular weight. After use, it can be completely decomposed by microorganisms in nature into carbon dioxide and water, originating from nature and returning to nature, truly achieving zero pollution.
The resin is a high-performance silk masterbatch suitable for 3D printing. It is blended with pure PLA at a certain ratio and can be processed and formed through standard 3D printing extrusion equipment. The extruded filament has a stable diameter, high gloss, and good toughness. It supports high-speed printing and is specially designed for FDM 3D printing extrusion applications.
Items | Test method | Unit | Value |
Density | ISO 1183 | g/cm3 | 1.24 |
Melt index | ISO 1133 | g/10min | 14-18 |
Melting point | ISO 11357 | ℃ | 130-150 |
Tensile Strength | ISO 527 | MPa | 36 |
Tensile modulus | ISO 527 | MPa | 3580 |
Elongation @ break | ISO 527 | % | 63 |
Bending Strength | ISO 178 | MPa | 76 |
Flexural modulus | ISO 178 | MPa | 3600 |
Notched impact strength | ISO 179 | KJ/m2 | 22.4 |
Unnotched impact strength | ISO 179 | KJ/m2 | 53 |
Heat Deflection Temperature | ISO 75 | ℃ | 50 |
Vicat softening temperature | ISO 306 | ℃ | 50 |
Note: The above data only represent general data | |||
Drying Conditions: After blending with PLA, dry at 50°C with hot air for 4 hours, or at 55°C in a tray oven for 3 hours.
Application Fields: After blending with PLA, it can be extruded into single-color, dual-color, tri-color, or rainbow-colored filament on different 3D filament production lines.
Extrusion Conditions: After blending with PLA, the recommended filament processing temperature is 200°C–240°C depending on equipment used by different manufacturers.
-