- * Description:
-
Description
Fast printing requires materials that can melt and cool quickly. However, to balance the speed of material melting and cooling, the physical properties of materials printed using fast techniques usually experience some decline. In order to provide 3D printed products with superior mechanical performance under fast printing conditions, we have conducted numerous tests on various rapid formulations. As a result, we have selectively chosen PLA+HS, also known as PLA+HS, which is specifically designed to match high-speed printing and offers enhanced toughness.
Features
Stronger resilience Excellent printability
Fast printing Lines are not easily brittle and broken
- * Product introduction video
-
- * Print model
-
| Density(g/cm3) | 1.24 |
| Melt Flow Index | 5.2（190℃/2.16kg） |
| Heat Distortion Temp(℃,0.45MPa) | 54 |
| Tensile Strength(MPa) (XY) | 53.12 |
| Tensile Strength(MPa)(Z) | 32 |
| Elongation at Break(%)(XY) | 4.01 |
| Elongation at Break(%)(Z) | 2.8 |
| Flexural Strength(MPa)(XY) | 83 |
| Flexural Strength(MPa)(Z) | 83 |
| Flexural Modulus(MPa)(XY) | 2900 |
| Flexural Modulus(MPa)(Z) | 2680.2 |
| IZOD Impact Strength(kJ/㎡)(XY) | 5.6 |
| IZOD Impact Strength(kJ/㎡)(Z) | 2.41 |
| Extruder Temperature(℃) | 210-230℃ |
| Bed temperature(℃) | 45-60℃ |
| Fan Speed(％) | 100% |
| Printing Speed(mm/S) | 50-350mm/s |
| Heated Bed | Need |
-
Download Materials