PLA Metta
Product description, mainly related to the product introduction and some table parameters, can be combined with graphics and text, and the content can be added, modified and deleted in the background column content management. Products can customize fields, and support dynamic fields and product subsidiary table information. Greatly enhance the practicality and applicability of the system, you are welcome to use it!
Color:
Net Weight：
Personal Purchase:
- * Description:
-
Description
Matte PLA filament has no smell when printing, which is safe and environmentally friendly; And the spool is made by reusing injection molding of PETG, ABS, PLA production waste and other industrial waste, and the outer box is made of recyclable paper. Make 3D printing more sustainable with the environmental protection concept; The matte PLA surface is delicate and does not show layer lines; The filament is not easy to break which made the printing is smooth for a long time without clogging. PLA matte filament can be used for early concept models and rapid prototyping. Low density, PLA-Matte single-roll filaments are 21% more than other matte PLA product print models.
Sellingpoint
Environmental friendly Excellent printability
Cost-effective Hard to break
High-speed printing Matte surface effect
Easy to peel off the support Low density
- * Product introduction video
-
- * Print model
-
| Density(g/cm3) | 1.329 |
| Melt Flow Index | 5.8（190℃/2.16kg） |
| Heat Distortion Temp(℃,0.45MPa) | 51 |
| Tensile Strength(MPa) (XY) | 25.976 |
| Tensile Strength(MPa)(Z) | 14.31 |
| Elongation at Break(%)(XY) | 7.23 |
| Elongation at Break(%)(Z) | 2.26 |
| Flexural Strength(MPa)(XY) | 42.6 |
| Flexural Strength(MPa)(Z) | 21.1 |
| Flexural Modulus(MPa)(XY) | 2249.05 |
| Flexural Modulus(MPa)(Z) | 1782.62 |
| IZOD Impact Strength(kJ/㎡)(XY) | 4.7 |
| IZOD Impact Strength(kJ/㎡)(Z) | 2.15 |
| Extruder Temperature(℃) | 190-230℃ |
| Bed temperature(℃) | 45-60℃ |
| Fan Speed(％) | 100% |
| Printing Speed(mm/S) | ＜200mm/s |
| Heated Bed | Need |
-
Download Materials