- * Description:
-
Description
Compared with normal materials, the printing speed is faster, the quality of the surface of printed object is higher, and the detail performance is better. The PLA-HS has good adaptability. By adjusting the materials, the high speed printing reduces the dependence on the cooling power of the printer and improves the printing performance. This high flow PLA can be used in concept models and rapid prototyping.
Features
Smooth flow without blocking.
Faster cooling and forming.
More suitable for high-speed printing.
- * Product introduction video
-
- * Print model
-
| Density(g/cm3) | 1.24 |
| Melt Flow Index | 5.2（190℃/2.16kg） |
| Heat Distortion Temp(℃,0.45MPa) | 53 |
| Tensile Strength(MPa) (XY) | 53.64 |
| Tensile Strength(MPa)(Z) | 30.46 |
| Elongation at Break(%)(XY) | 4.34 |
| Elongation at Break(%)(Z) | 2.43 |
| Flexural Strength(MPa)(XY) | 85.29 |
| Flexural Strength(MPa)(Z) | 48 |
| Flexural Modulus(MPa)(XY) | 2962.32 |
| Flexural Modulus(MPa)(Z) | 2684.19 |
| IZOD Impact Strength(kJ/㎡)(XY) | 4.77 |
| IZOD Impact Strength(kJ/㎡)(Z) | 2.01 |
| Extruder Temperature(℃) | 210-230℃ |
| Bed temperature(℃) | 45-60℃ |
| Fan Speed(％) | 100% |
| Printing Speed(mm/S) | 50-300mm/s |
| Heated Bed | Need |
-
Download Materials