- * Description:
-
Description
PETG+HS, PETG Formula Newly Optimized for Faster and Superior Cooling Solidification, Compatible with High-Speed Printing, Material Adhesion to Nozzle during Printing Issues Optimized, Reducing the Likelihood of Poor Printing, Cost-Effective Waterproof, Chemical Resistant, High Toughness, and Fast Printing Material.
Sellingpoint
High Toughness
Chemical Resistance
WaterproofNotes
Turn on the Z seam alignment . Turn off the Z-axis lifting with drawing.
Slower the printing speed.
- * Product introduction video
-
- * Print model
-
| Density(g/cm3) | 1.26 |
| Melt Flow Index | 24（250℃/2.16kg) |
| Heat Distortion Temp(℃,0.45MPa) | 68 |
| Tensile Strength(MPa) (XY) | 49.52 |
| Tensile Strength(MPa)(Z) | 39.6 |
| Elongation at Break(%)(XY) | 8 |
| Elongation at Break(%)(Z) | 5.05 |
| Flexural Strength(MPa)(XY) | 70.2 |
| Flexural Strength(MPa)(Z) | 46 |
| Flexural Modulus(MPa)(XY) | 1915.89 |
| Flexural Modulus(MPa)(Z) | 1506.88 |
| IZOD Impact Strength(kJ/㎡)(XY) | 6.07 |
| IZOD Impact Strength(kJ/㎡)(Z) | 2.05 |
| Extruder Temperature(℃) | 220-260℃ |
| Bed temperature(℃) | 75-90℃ |
| Fan Speed(％) | 100% |
| Printing Speed(mm/S) | 40-300mm/s |
| Heated Bed | Need |
| Printing Suggestions | Dry at 60℃ for 8 hours |
| Need to Dry | √ |
-